   Zarif Mosavar Co. produces its products by using the latest technologies and modern production equipment. Produc-tion equipments are listed below:

  • Five production lines for different polyester fibers, recycled polyester, polyamide, and polypropylene with the daily ca-pacity of 100 tons, and a line for washing crushed polyester material
  • Three production lines for BCF Yarn, heat set, frieze and cabling yarn with the daily capacity of 20 tons.
  • Production line of packing plastic materials with the daily capacity of 3 tons .
  • Production line of NGR recycles granules with the capacity of 6 tons per day.
  • Equipped QC laboratory with all the required equipment for yarn and fiber production processes It is to note that all the exist-ing production and laboratory equipment are made in well-known European companies from France, England, to italy.

PRODUCTS


FIBERS & YARNS BCF

In the field of Melt spinning, Zarif Mosavar products are divided into two main groups of fibers & BCF Yarns.

Man - made fibres made of:
polyester (virgin and recycled), poly propylene, and polyamide beside BCF polypropylene and polyamide yarn, (heat set, frieze, md cabling).

Product Group Material Type 1 Type 2 Measuring Unit Refworks Color
Fiber PET Recycle Solid > 3 To Order To Order
Fiber Polyester Virgin Hallow > 2 To Order To Order
Fiber PET Recycle Hallow > 3 To Order To Order
Fiber Polypropylene Virgin Solid > 2 To Order To Order
Fiber Polypropylene Virgin Concrete > 2 To Order To Order
Fiber PET Recycle Concrete > 2 To Order To Order
Fiber Polyamide Virgin Solid > 2 To Order To Order
Fiber Polypropylene Virgin Hydrophilic > 2 To Order To Order
Fiber Polyester Virgin . Recycle Solid > 3 To Order To Order
Fiber PET Recycle Melange > 3 To Order To Order
Fiber Polypropylene Virgin High Tenacity > 3 To Order To Order
Fiber Polypropylene Heat Set Frieze > 1400 Two Folded To Order
Thread Polypropylene Heat Set Frieze > 2800 Single Folded To Order
Thread Polyamide Heat Set Frieze > 800 Single Folded To Order
Thread Polyester Heat Set Frieze > 800 Single Folded To Order
Thread Polyester Heat Set Frieze > 1600 Two Folded To Order
Granule Polyester Pure Recycle PSU MFI from 5 to 25 To Order
Granule Polypropylene . Polyester Mixed Recycle PPMA MFI from 5 to 25 To Order
Granule Polypropylene Mixed Recycle PPU MFI from 5 to 25 To Order
Plastic Polypropylene - Virgin * Single & Double Folded Thickness 50-200 Transparent

COMPETITIVE

ADVANTAGES


   Zarif-Mosavar group is supported by the ownership of Regal Petrochemical and Tis-Masterbatch companies and obviously there is no specific limitation in providing of row material.

TECHNICAL

SPECIFICATIONS


   Technical specifications of some pf the organization products are as follows:

Denier 3 Polyester Fibers
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 51 ± 5 . 64 ± 5 mm A ISO6989
Extraction Oil 0.2 ± 0.05 % B ISIRI-30
Strength Min: 3 Gram Force / Denier B ISO5079
Elongation of Length 50 ± 10 % B ISO5079
Elegance 3 ±10% Denier A ISO1973
Humidity Max: 1 % A ISIRI-30
Contraction -2 - 0 % B ASTM D4974
Color According to Specimen - B Control Sample
No . of Curls 50 ± 10 No. / Decimeter B Domestic Method
Denier 6 Polyester Fibers
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 64 ± 5 mm A ISO6989
Extraction Oil 0.15 - 0.25 % B ISIRI-30
Strength Min: 3 Gram Force / Denier B ISO5079
Elongation of Length 55 ± 15 % B ISO5079
Elegance 6 ±10% Denier A ISO1973
Humidity Max: 1 % A ISIRI-30
Contraction -2 - 1 % B ASTM D4974
Color According to Specimen - B Control Sample
No . of Curls 45 ± 10 No. / Decimeter B Domestic Method
Denier 6 Polypropylene Fibers (For Export)
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 90 ± 5 . 110 ± 5 mm A ISO6989
Extraction Oil 0.4 ± 0.05 % A ISIRI-30
Elegance 6 ± %10 Denire A ISO1973
Tearing Strength Min: 45 Centinewton / Tex A ASTM D3822
Elongation of Length Min: 40 % B ASTM D3822
Humidity Max: 1 % A ISIRI-30
Contraction Max: 3 % C ASTM D4974
Color According to Control Sample - B Control Sample
Denier 15 Polyester Fibers
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 6 ± 5 mm A ISO6989
Extraction Oil 0.2 - 0.4 % B ISIRI-30
Strength Min: 3 Gram Force / Denier B ISO5079
Elongation of Length Min: 60 % B ISO5079
Elegance 15 ± 10% Denier A ISO1973
Humidity Max: 1 % B ISIRI-30
Contraction Max: 1 % B ASTM D4974
Color Fully Dispersed in Water - B Control Sample
No . of Curls 26 ± 6 No. / Decimeter A Domestic Method
Denier 17 Polyester Fibers
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 64 ± 5 mm B ISO6989
Extraction Oil 0.2 - 0.4 % C ISIRI-30
Elegance 17 ± 10% Denier B ISO5079
Strength Min: 3 Gram Force / Denier B ISO5079
Elongation of Length Min: 100 % B ISO1973
Humidity Max: 1 % B ISIRI-30
Contraction Max: 1 % C ISIRI-30
Contraction Max: 5 % B ASTM D4974
Color According to Specimen - B Control Sample
No . of Curls 25 - 30 No. / Decimeter B Domestic Method
Self - Colored 35T Diameter ConcreteFibers
Product Specificition Acceptable Range Measuring Unit Grade Test Reference
Length of Fibers 6 ± 1.5 . 12 ± 1.5 . 18 ± 1.5 mm B ISO6989
Extraction Oil 0.5 - 0.6 % A PL-OPAO
Diameter 35 ± 1.7 Micron B Domestic Laboratory
Tearing Strength Min: 345 Centinewton / mm2 B ASTM D3822
Elongation of Length Max: 80 % C ASTM D3822
Humidity Max: 1 % B PL-MERO
External Particles Without External Particles % A Control Sample
Dispersion Fully Dispersed in Water % B Domestic Method
Color According to Specimen - B Control Sample
No . of Curls 25 - 30 No. / Decimeter B Domestic Method